PPO(聚苯醚)|NORYL|PX9406/沙伯基础/物性表参数

日期：2020-11-06 03:09:19 编辑：科思德塑胶来源：科思德塑胶浏览：564

沙伯基础(SABIC)NORYL PPO PX9406是一种聚苯醚(PPO) 无溴，无氯，阻燃，提高了生产力和可靠性，252F HDT，UL94 V-0等级，应用于电子/电子市场室内/室外应用。

以下是PPO(聚苯醚)PX9406/沙伯基础(NORYL)物性表参数

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
FLAME CHARACTERISTICS	¹⁾
Glow Wire Flammability Index 960°C, passes at	²⁾	3.2	mm	IEC 60695-2-12
Oxygen Index (LOI)		36	%	ISO 4589
MECHANICAL
Tensile Stress, yield, 50 mm/min		55	MPa	ISO 527
Tensile Stress, break, 50 mm/min		45	MPa	ISO 527
Tensile Strain, yield, 50 mm/min		4	%	ISO 527
Tensile Strain, break, 50 mm/min		10	%	ISO 527
Tensile Modulus, 1 mm/min		2400	MPa	ISO 527
Flexural Stress, yield, 2 mm/min		70	MPa	ISO 178
Flexural Modulus, 2 mm/min		2100	MPa	ISO 178
Ball Indentation Hardness, H358/30		95	MPa	ISO 2039-1
IMPACT
Izod Impact, notched 80104 +23°C		12	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C		7	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm		11	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80104 sp=62mm		7	kJ/m²	ISO 179/1eA
THERMAL
Thermal Conductivity		0.22	W/m-°C	ISO 8302
CTE, 23°C to 80°C, flow		7.E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow		9.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C		PASSES	-	IEC 60695-10-2
Ball Pressure Test, approximate maximum		125	°C	IEC 60695-10-2
Vicat Softening Temp, Rate A/50		135	°C	ISO 306
Vicat Softening Temp, Rate B/50		125	°C	ISO 306
Vicat Softening Temp, Rate B/120		130	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm		125	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm		110	°C	ISO 75/Ae
PHYSICAL
Mold Shrinkage on Tensile Bar, flow		0.5-0.7	%	SABIC method
Density		1.1	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)		0.2	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)		0.06	%	ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg		10	cm³/10 min	ISO 1133
ELECTRICAL
Volume Resistivity		1.E+15	Ohm-cm	IEC 60093
Surface Resistivity, ROA		>1.E+15	Ohm	IEC 60093
Dielectric Strength, in oil, 0.8 mm		33	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 1.6 mm		26	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 3.2 mm		16	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz		2.6	-	IEC 60250
Dissipation Factor, 50/60 Hz		0.007	-	IEC 60250
Dissipation Factor, 1 MHz		0.003	-	IEC 60250
Relative Permittivity, 50/60 Hz		2.7	-	IEC 60250
Injection Molding
Drying Temperature		80-100	°C
Drying Time		2-3	hrs
Melt Temperature		280-300	°C
Nozzle Temperature		260-280	°C
Front - Zone 3 Temperature		280-300	°C
Middle - Zone 2 Temperature		260-280	°C
Rear - Zone 1 Temperature		240-260	°C
Hopper Temperature		60-80	°C
Mold Temperature		90-120	°C