PPO(聚苯醚)GFN1720/沙伯基础(Noryl)物性表参数

日期：2020-10-29 02:30:26 编辑：科思德塑胶来源：科思德塑胶浏览：619

沙伯基础(SABIC)Noryl PPO GFN1720是一种加20%玻璃纤维增强，注塑级别PPE + PS混合(聚苯醚)，这种改性聚苯醚树脂的设计目的是提供一个平衡的热量，强度和电气性能，Noryl GFN1720有多种颜色可供选择，可能是点火线圈，筒子和其他需要电绝缘性能的应用的材料。
PPO GFN1720

以下是PPO(聚苯醚)GFN1720/沙伯基础(Noryl)物性表参数

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
FLAME CHARACTERISTICS	¹⁾
UL Yellow Card Link		E45329-236755	-	-
UL Recognized, 94HB Flame Class Rating		≥1.5	mm	UL 94
Glow Wire Flammability Index 960°C, passes at	²⁾	3.2	mm	IEC 60695-2-12
Oxygen Index (LOI)		23	%	ISO 4589
MECHANICAL
Tensile Stress, yld, Type I, 5 mm/min		90	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min		90	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min		2.5	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min		3	%	ASTM D 638
Tensile Modulus, 5 mm/min		5500	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span		145	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span		4800	MPa	ASTM D 790
Taber Abrasion, CS-17, 1 kg		45	mg/1000cy	SABIC method
Tensile Stress, yield, 5 mm/min		90	MPa	ISO 527
Tensile Stress, break, 5 mm/min		90	MPa	ISO 527
Tensile Strain, yield, 5 mm/min		2	%	ISO 527
Tensile Strain, break, 5 mm/min		2	%	ISO 527
Tensile Modulus, 1 mm/min		6000	MPa	ISO 527
Flexural Stress, break, 2 mm/min		135	MPa	ISO 178
Flexural Modulus, 2 mm/min		4500	MPa	ISO 178
Ball Indentation Hardness, H358/30		100	MPa	ISO 2039-1
IMPACT
Izod Impact, notched, 23°C		60	J/m	ASTM D 256
Izod Impact, notched, -30°C		50	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C		14	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C		25	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80104 -30°C		25	kJ/m²	ISO 180/1U
Charpy 23°C, Unnotch Edgew 80104 sp=62mm		25	kJ/m²	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80104 sp=62mm		25	kJ/m²	ISO 179/1eU
THERMAL
Vicat Softening Temp, Rate B/50		181	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed		171	°C	ASTM D 648
CTE, -40°C to 40°C, flow		4.E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow		5.E-05	1/°C	ASTM E 831
Thermal Conductivity		0.26	W/m-°C	ISO 8302
CTE, 23°C to 80°C, flow		3.E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow		7.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C		PASSES	-	IEC 60695-10-2
Ball Pressure Test, approximate maximum		165	°C	IEC 60695-10-2
Vicat Softening Temp, Rate A/50		180	°C	ISO 306
Vicat Softening Temp, Rate B/50		170	°C	ISO 306
Vicat Softening Temp, Rate B/120		180	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm		170	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm		160	°C	ISO 75/Ae
Relative Temp Index, Elec	¹⁾	65	°C	UL 746B
Relative Temp Index, Mech w/impact	¹⁾	65	°C	UL 746B
Relative Temp Index, Mech w/o impact	¹⁾	65	°C	UL 746B
PHYSICAL
Specific Gravity		1.24	-	ASTM D 792
Mold Shrinkage on Tensile Bar, flow		0.2-0.4	%	SABIC method
Mold Shrinkage, flow, 3.2 mm		0.2-0.4	%	SABIC method
Melt Flow Rate, 300°C/5.0 kgf		4.5	g/10 min	ASTM D 1238
Density		1.24	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)		0.15	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)		0.06	%	ISO 62
Melt Volume Rate, MVR at 300°C/10.0 kg		11	cm³/10 min	ISO 1133
ELECTRICAL
Volume Resistivity		1.E+15	Ohm-cm	IEC 60093
Surface Resistivity, ROA		>1.E+15	Ohm	IEC 60093
Dielectric Strength, in oil, 0.8 mm		30	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 1.6 mm		26	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 3.2 mm		16	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz		2.6	-	IEC 60250
Dissipation Factor, 50/60 Hz		0.006	-	IEC 60250
Dissipation Factor, 1 MHz		0.002	-	IEC 60250
Comparative Tracking Index	²⁾	200	V	IEC 60112
Relative Permittivity, 50/60 Hz		2.7	-	IEC 60250
Injection Molding
Drying Temperature		110-120	°C
Drying Time		2-4	hrs
Melt Temperature		290-330	°C
Nozzle Temperature		290-310	°C
Front - Zone 3 Temperature		310-330	°C
Middle - Zone 2 Temperature		290-310	°C
Rear - Zone 1 Temperature		270-290	°C
Hopper Temperature		60-80	°C
Mold Temperature		80-120	°C