沙伯基础创新塑料（SABIC）LEXAN PC 3413HF是一种注塑、含脱模剂，阻燃等级，玻璃纤维填充30%聚碳酸酯树脂，溶化体积流率（MVR)(330°C/2.16 kg)40.0cm³/10min，它有UL94 V1-厚度是2mm的评级，并可在各种不透明的颜色选项。

以下是PC(聚碳酸酯)3413HF/沙伯基础(SABIC)物性表参数

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, brk, Type I, 5 mm/min	99	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2	%	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	153	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	6610	MPa	ASTM D 790
IMPACT
Izod Impact, notched, 23°C	69	J/m	ASTM D 256
THERMAL
HDT, 1.82 MPa, 6.4 mm, unannealed	137	°C	ASTM D 648
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B
PHYSICAL
Specific Gravity	1.44	-	ASTM D 792
Melt Flow Rate, 300°C/5.0 kgf	40	g/10 min	ASTM D 1238
ELECTRICAL
Hot Wire Ignition {PLC)	1	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	4	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	3	PLC Code	UL 746A
FLAME CHARACTERISTICS
UL Yellow Card Link	E121562-220882	-	-
UL Recognized, 94V-1 Flame Class Rating	1.47	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating	2.99	mm	UL 94
Injection Molding
Drying Temperature	120	°C
Drying Time	3-4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	310-330	°C
Nozzle Temperature	305-325	°C
Front - Zone 3 Temperature	310-330	°C
Middle - Zone 2 Temperature	300-320	°C
Rear - Zone 1 Temperature	290-310	°C
Mold Temperature	80-115	°C
Back Pressure	0.3-0.7	MPa
Screw Speed	40-70	rpm
Shot to Cylinder Size	40-60	%
Vent Depth	0.025-0.076	mm