VALOX(沙伯基础)VX5022/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX VX5022 PBT是一种加20%玻璃纤维增强PBT+PC共混物，具有低翘曲性能,这个等级是5021，减少翘曲。
 |
沙伯基础创新塑料的VALOX VX5022 PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)VX5022/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 125 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 125 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 7300 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 145 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5800 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 110 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 110 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 7100 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 6300 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 205 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 122 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 55 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 50 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 650 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 645 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 65 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 200 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 180 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 2.49E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.87E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.43E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.12E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 200 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 145 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 180 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.39 | - | ASTM D 792 | |
| Filler Content | 20 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.8 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.3-0.5 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.9 | % | SABIC method | |
| Melt Flow Rate, 250°C/2.16 kgf | 16 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 265°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 266°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Density | 1.39 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.1 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 13 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 28 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 40 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 215 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.3 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.014 | - | ASTM D 150 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+16 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+16 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 100 Hz | 3.3 | - | IEC 60250 | |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 100 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 | |
| Comparative Tracking Index, M | 100 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Flammability Index 850°C, passes at | 2 | mm | IEC 60695-2-12 | |
| Oxygen Index (LOI) | 23 | % | ISO 4589 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：8725 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：8459 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：7577 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：6885 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：6246 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：5583 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：5480 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：5142 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：5140 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：5065 -
COC(环烯烃共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一种烯烃聚合物(COP)具有优异的光学性能，可用于制造相机和激光打印机的光学部件，比重是1.01g/cm(ASTM D792)，熔流率（熔体流动速率）(280C/2.16 kg)是25g/10 min，ZEO
浏览量：4859 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：4828 -
PC(聚碳酸酯)L-1250Y|嘉兴帝人|物性表参数嘉兴帝人Panlite PC L-1250Y 是一款熔融体积流量是8MVR，特性是 脱模性能良好, 中等粘性 ，通用级应用，在Japan实现工业化生产的聚碳酸酯树脂，长期以来，帝人一直致力于其性能的提高和
浏览量：4756 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：4710 -
PC(聚碳酸酯)PC-1100|乐天化学(LOTTE CHEMI···乐天化学的LOTTE Chemical HOPELEX PC PC-1100 是一种聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高强度、FDA/EU 食品容器认证，用于普通注塑产品。 以下是PC(聚碳酸酯)PC-1100/韩国乐天化学
浏览量：4580
推荐文章
-
RYTON(索尔维)R-4-230BL|PPS(聚苯硫醚)物性表参数
SOLVAY(索尔维0Ryton PPS R-4-230BL 是一款添加40%玻璃纤维，黑色聚苯硫醚原料，特性是毛边少、流动性好、强度高，材料优势是可精密成型、阻燃、良好的电气性能、热固性树脂替代材料、耐
-
PC(聚碳酸酯)943X|沙伯基础(SABIC)物性表参数
SABIC(沙伯基础创新塑料)LEXAN PC 943X 是一种抗UV稳定的高流动冲击改性注塑(IM)级产品，该树脂提供UL94 V0 1.5mm的阻燃性能，是非溴、非氯阻燃性能，低温延展性和优异的加工性能，与标准
-
TPU(热塑性聚氨酯)58244/路博润(Lubrizol)物性表参数
路博润(Lubrizol)ESTANE TPU 58244是一种聚醚型无卤阻燃热塑性聚氨酯，肖氏硬度90A，专为性能优异的挤塑和注塑部件而设计，主要用于挤塑和注塑应用。以下是TPU(热塑性聚氨酯)58244/路博润(Lubrizol)物性表参数原厂资料ESTANE 58244.pdf产品特性阻燃无卤成型方式挤出技术参数物理性能值/单位测试标准测试条件比重1.19 -ASTM
-
TPE(热塑性弹性体)TF6FHT/凯柏胶宝/物性表参数
凯柏胶宝KRAIBURG热塑宝K TPE TF6FHT 是一款透明, 硬度60A的FC/ht系列TPE材料,用于食品接触应用的高透明度材料解决方案,该系列特点之一是卓越的 PP包胶性能，典型应用：剃须刀、功能和设计
-
PA66(尼龙66)AC30|朗盛(LANXESS)物性表参数
朗盛(LANXESS)Durethan PA66 AC30是一种无强化，注塑成型，热老化稳定，提高冲击强度尼龙树脂,根据特定的材料及所需等级，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度，除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提
-
POM(聚甲醛树脂)2010|旭化成(AsahiKASEI)物性表参数
旭化成(AsahiKASEI)TENAC(铁耐克)POM 2010是超高抗冲击，高分子量均聚的聚甲醛树脂，密度 1.41(g/cm³)，弯曲模量2700(MPa) ，简支梁缺口冲击强度15.0(kJ/m²) ，典型用途领域包括工程/工业配件、房屋和汽车行业。TENAC POM 2010 ISO参数PDF文档以下是POM(聚甲醛树脂)2010|旭化成(AsahiKASEI)物性表参数物理性能额定值单位
-
XYRON(采龙)L542Z|旭化成|PPO(聚苯醚)物性表参数
旭化成XYRON PPO L542Z 是一种加入20%填料,低翘曲性, 高刚性,高流动阻燃级PPE/PS原料，特点: 良好的耐热性、尺寸稳定性和机械性能，应用领域: 汽车零件，电气和电子零件，工业零件，
-
PC(聚碳酸酯)SLX1432/沙伯基础LEXAN/物性表参数
美国沙伯基础SABIC LEXAN PC SLX1432介绍： LEXAN PC SLX1432 树脂是中粘度PC共聚物具有增强的UV稳定性和添加的释放剂。可以在不透明的颜色。典型的最小颜色公差极限是DE CMC 1.0。。Lexan SLX143
-
Zytel(陶氏杜邦)70G25HSL|PA66(尼龙66)物性表参数
Dupont Zytel 70G25HSL PA66 是一种一种13% 玻纤增强尼龙66树脂,包括良好的机械和物理性能，例如高机械强度，刚性和韧性之间良好的平衡，良好的高温性能、电性能和阻燃性能，优异的耐磨损
-
Xytron(帝斯曼)G4010E|PPS(聚苯硫醚)物性表参数
荷兰帝斯曼 Xytron G4010E PPS 是一种40%玻纤增强, 冲击改性, DMS PPS塑胶原料,Xytron G4010E是帝斯曼工程塑料中的高性能塑料，基料为PPS（聚苯硫醚）,拥有绝佳的耐化学性，尺寸稳定性，天生的