VALOX(沙伯基础)K4560/PBT热塑性聚酯/物性表参数

日期：2020-04-20 01:34:28 编辑：科思德塑胶来源：科思德塑胶浏览：325

沙伯基础创新塑料SABIC的VALOX K4560 PBT是一种加30%玻璃增强PBT，水解稳定，冲击改性，高流动，汽车连接器。

以下是VALOX(沙伯基础)K4560/PBT热塑性聚酯/物性表参数

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 5 mm/min	112	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	112	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	3	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	3	%	ASTM D 638
Tensile Modulus, 5 mm/min	8840	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	173	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	7200	MPa	ASTM D 790
Tensile Stress, break, 5 mm/min	120	MPa	ISO 527
Flexural Stress, break, 2 mm/min	175	MPa	ISO 178
Flexural Modulus, 2 mm/min	7400	MPa	ISO 178
IMPACT
Izod Impact, unnotched, 23°C	817	J/m	ASTM D 4812
Izod Impact, notched, 23°C	96	J/m	ASTM D 256
Izod Impact, unnotched 80104 +23°C	52	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	11	kJ/m²	ISO 180/1A
THERMAL
HDT, 0.45 MPa, 3.2 mm, unannealed	220	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	200	°C	ASTM D 648
Vicat Softening Temp, Rate B/120	204	°C	ISO 306
PHYSICAL
Specific Gravity	1.5	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.6-0.8	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	1-1.2	%	SABIC method
Melt Volume Rate, MVR at 250°C/2.16 kg	12	cm³/10 min	ISO 1133
Glass Fiber Content	30	%	ISO 3451
AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III
Tensile Stress, brk, Type I, 50 mm/min	96	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	102	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2.2	%	ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span	7400	MPa	ASTM D 790
Flexural Strain, 1.3 mm/min, 50 mm span	4.5	%	ASTM D 790
Instrumented Impact, Total Energy, 23°C	8	J	ASTM D 3763
PROPERTIES AFTER 1008 HOURS AT 125?C
Tensile Stress, brk, Type I, 5 mm/min	115	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	4	%	ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span	7100	MPa	ASTM D 790
Flexural Strain, 1.3 mm/min, 50 mm span	4.2	%	ASTM D 790
Instrumented Impact, Total Energy, 23°C	7	J	ASTM D 3763
AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV
Tensile Stress, brk, Type I, 5 mm/min	107	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2.5	%	ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span	8000	MPa	ASTM D 790
Flexural Strain, 1.3 mm/min, 50 mm span	4	%	ASTM D 790
Instrumented Impact, Total Energy, 23°C	6	J	ASTM D 3763
PROPERTIES AFTER 1008 HOURS AT 155?C
Tensile Stress, brk, Type I, 5 mm/min	110	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	4	%	ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span	7500	MPa	ASTM D 790
Flexural Strain, 1.3 mm/min, 50 mm span	4.2	%	ASTM D 790
Injection Molding
Drying Temperature	60-75	°C
Drying Time	4-6	hrs
Drying Time (Cumulative)	8	hrs
Maximum Moisture Content	0.05	%
Melt Temperature	250-265	°C
Nozzle Temperature	245-260	°C
Front - Zone 3 Temperature	250-265	°C
Middle - Zone 2 Temperature	245-260	°C
Rear - Zone 1 Temperature	240-255	°C
Mold Temperature	65-90	°C
Back Pressure	0.3-0.7	MPa
Screw Speed	50-80	rpm
Shot to Cylinder Size	40-80	%
Vent Depth	0.025-0.038	mm

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.

上一页：VALOX(沙伯基础)K4530/PBT热塑性聚酯/物性表参数下一页：VALOX(沙伯基础)PDR4922/PBT热塑性聚酯/物性表参数

返回首页返回物性参数列表

VALOX(沙伯基础)K4560/PBT热塑性聚酯/物性表参数

热门文章

推荐文章