VALOX(沙伯基础)735/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX 735 PBT是一种加40%玻璃/矿物，优异的热工性能/低收缩,电动加热设备，适配器环，烤箱烤架等,提供黑色/自然色。
 |
沙伯基础创新塑料的VALOX 735 PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)735/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 95 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 95 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 10400 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8300 | MPa | ASTM D 790 | |
| Taber Abrasion, CS-17, 1 kg | 64 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 90 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 90 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 10000 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 130 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 130 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 2 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 8300 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 144 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 124 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 40 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 30 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 560 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 520 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 60 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 55 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 50 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 7 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 7 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 185 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 215 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 190 | °C | ASTM D 648 | |
| Thermal Conductivity | 0.36 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 2.28E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.53E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.18E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.4E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 180 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 180 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 190 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.62 | - | ASTM D 792 | |
| Filler Content | 40 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.6 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.8 | % | SABIC method | |
| Melt Flow Rate, 266°C/5.0 kgf | 20 | g/10 min | ASTM D 1238 | |
| Density | 1.62 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.96 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 1 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 3 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 15 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 160 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 45 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 22 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 45 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 22 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.008 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.017 | - | IEC 60250 | |
| Relative Permittivity, 50/60 Hz | 3.5 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 0.81 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 4 - 6 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 260 - 285 | °C | ||
| Nozzle Temperature | 265 - 275 | °C | ||
| Front - Zone 3 Temperature | 260 - 280 | °C | ||
| Middle - Zone 2 Temperature | 255 - 280 | °C | ||
| Rear - Zone 1 Temperature | 240 - 260 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 60 - 110 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：10052 -
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：9334 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：8614 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：7509 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：6930 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：6438 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：6096 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：5791 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：5750 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：5473 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：5337 -
COC(环烯烃共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一种烯烃聚合物(COP)具有优异的光学性能，可用于制造相机和激光打印机的光学部件，比重是1.01g/cm(ASTM D792)，熔流率（熔体流动速率）(280C/2.16 kg)是25g/10 min，ZEO
浏览量：5281 -
PA12(尼龙12)TR90|瑞士EMS化学|物性表参数科思德塑胶网站提供瑞士EMS化学PA12 TR90的物性表参数下载，并且有Grilamid PA12 TR90塑胶粒销售，为您提供详细的瑞士EMS化学PA12(尼龙12)TR90资料以及报价。
浏览量：5273 -
TRITAN(美国伊士曼)TX1501HF/PCTG(共聚聚酯···美国伊士曼TRITAN PCTG TX1501HF 是一种伊士曼TRITAN的高流动级材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相对于伊士曼TRITAN共聚酯TX1001，其他突出的特点包括良好的韧性，水解稳定性，耐热性
浏览量：5190 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：5173
推荐文章
-
PEEK(聚醚醚酮)1000G/赢创德固赛/物性表参数
赢创德固赛 VESTAKEEP PEEK 1000G 是无筋,低粘度,easy-flowing低至中等粘度的产品，如齿轮零件，医疗技术的零件，薄膜，被单和半成品。 40多年来，Evonik一直在生产高性能聚合物，在市场上备
-
PBT(聚对苯二甲酸丁二酯)5010G30TZ|三菱工程塑料|物性表参数
三菱工程塑料NOVADURAN PBT 5010G30TZ是一种聚对苯二甲酸丁二酯(PBT)材料，熔融体积流量（MVR)(cm³/10min)是65((250°C/5.0kg))，简支梁缺口冲击强度(kJ/m²)是7.0(23°C)，含有的填充物为30% 玻璃纤维增强材料，加工方式为：注射成型，NOVADURAN 5010G30TZ主要特性为:耐热，非阻燃/额定火焰。以下是PBT(聚对苯二甲酸
-
PA66(尼龙66)A205F|索尔维(SOLVAY)物性表参数
索尔维(SOLVAY)(罗地亚)TECHNYL PA66 A205F是一种无增强尼龙66(PA66)树脂，快的成型周期，流动性高，用于注射成型，该产品用于薄壁部件、紧固件、连接器。以下是PA66(尼龙66)A205F|索尔维(SOLVAY)物性表参数物理性能干燥调节后的单位制测试方法密度 1.14--g/cm³ISO 1183/A收缩率 内部方法 垂直流动
-
TPE/K TC7COZ/TPE物性参数
德国胶宝Kraiburg THERMOLAST TPE K TC7COZ 物性参数 K TC7COZ是德国胶宝公司Kraiburg THERMOLAST塑性弹性体TPE型号之一 德国胶宝Kraiburg THERMOLAST TPE K TC7COZ 物性参数 以下是德国胶宝Kraiburg THERMOLAST TPE
-
PP(聚丙烯)J-160H|乐天化学(LOTTE CHEMICAL)物性表参数
乐天化学(LOTTE CHEMICAL)PP J-160H是一种注塑级聚丙烯聚合物，比重(23°C)是0.9克/厘米³，熔体流动速率(230°C/2.16kg)是17克/10分钟，该等级设计用于在常规注塑设备中加工，具有高流动性，高刚度，热稳定性，耐划伤和高表面光泽度，用于生活用品、食品容器、文具类、一次性用品等。以下是PP(聚丙烯)J-160H|乐天化学(LO
-
塞拉尼斯TPV 291-60B150|SANTOPRENE物性表参数
Celanese(塞拉尼斯)SANTOPRENE(山都坪)TPV 291-60B150是一种热塑性硫化弹性体，它是热塑性弹性体（TPE）系列中的一种可着色的特种热塑性硫化弹性体（TPV）， 它专为与 PC、ABS、PC/ABS 和 PMMA 粘结而配制，适用于要求硬/软材料组合的应用，这一牌号的山都平TPV是剪切速率依赖型产品，可在常规热塑性注塑成型或 挤出成型
-
PPS(聚苯硫醚)1140A64|宝理塑料|物性表参数
日本宝理 PPS DURAFIDE 1140A64 是一种GF增强 ,标准, 低溢的聚苯硫醚,其用途不仅限于电子零件。可应用于灯座、水泵、各种电装部件等，作为汽车部件、OA设备、AV设备的功能部件的材料也可
-
LEONA(尼胺龙)CR103(旭化成)PA66(尼龙66)物性表参数
日本旭化成Leona PA66 CR103 是一款加矿物填料特殊复合材料等级尼龙树脂，典型的特性是尺寸稳定性良好; 低摩擦系数; 热稳定性; 润滑，可以应用于电气/电子应用领域; 工业应用; 构件; 汽
-
PC（聚碳酸酯）EXL1434T|沙伯基础|物性表参数
沙伯基础LEXAN PC EXL1434T聚碳酸酯(PC)硅氧烷共聚物树脂是UV稳定透明注塑级，该树脂具有极低温(-40℃)的延展性，结合介质流动特性和优异的加工性能，与标准PC相比，IM循环时间更短，LEXAN EXL1434T树脂是一种UV稳定的通用产品，可用于透明和不透明的颜色，是广泛应用的材料。以下是PC（聚碳酸酯）EXL1434T|沙伯基础|物性表
-
PC(聚碳酸酯)6457/科思创(Makrolon)物性表参数
科思创(Covestro)模克隆(Makrolon) PC 6457 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 12cm cm /10 min，中粘度，带有脱模剂，阻燃UL 94 v-0/3.0 mm，应用于多种阻燃产品。 以下是PC(聚碳酸酯