VALOX(沙伯基础)420/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX 420 PBT是一种加30%GR，具有优异的强度、刚度和尺寸稳定性,高耐热性,产品电器手柄，聚光灯，电动马达，连接器。
 |
沙伯基础创新塑料的VALOX 420 PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)420/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 145 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 145 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 10300 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8000 | MPa | ASTM D 790 | |
| Taber Abrasion, CS-17, 1 kg | 19 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 135 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 135 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 10250 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 205 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 200 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 4 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 8500 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 125 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 120 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 55 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 50 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 970 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 970 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 110 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 105 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 105 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 45 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 10 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 9 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -40°C | 5 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 11 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 11 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 210 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D 648 | |
| Thermal Conductivity | 0.19 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 2.09E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.67E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.05E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.78E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 215 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 205 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.53 | - | ASTM D 792 | |
| Filler Content | 30 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.7 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-1 | % | SABIC method | |
| Melt Flow Rate, 266°C/5.0 kgf | 55 | g/10 min | ASTM D 1238 | |
| Density | 1.53 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.26 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 12 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 30 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 45 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 130 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | ASTM D 149 | |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 1 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, shorttime, 1.0mm | 19 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 | |
| Comparative Tracking Index | >600 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 0.84 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 6 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 775 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 3.0 mm | 825 | °C | IEC 60695-2-13 | |
| Injection Molding | ||||
| Drying Temperature | 120 | °C | ||
| Drying Time | 3-4 | hrs | ||
| Drying Time (Cumulative) | 12 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250-265 | °C | ||
| Nozzle Temperature | 245-260 | °C | ||
| Front - Zone 3 Temperature | 250-265 | °C | ||
| Middle - Zone 2 Temperature | 245-260 | °C | ||
| Rear - Zone 1 Temperature | 240-255 | °C | ||
| Mold Temperature | 65-90 | °C | ||
| Back Pressure | 0.3-0.7 | MPa | ||
| Screw Speed | 50-80 | rpm | ||
| Shot to Cylinder Size | 40-80 | % | ||
| Vent Depth | 0.025-0.038 | mm |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：8718 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：8452 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：7572 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：6881 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：6244 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：5579 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：5480 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：5138 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：5137 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：5064 -
COC(环烯烃共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一种烯烃聚合物(COP)具有优异的光学性能，可用于制造相机和激光打印机的光学部件，比重是1.01g/cm(ASTM D792)，熔流率（熔体流动速率）(280C/2.16 kg)是25g/10 min，ZEO
浏览量：4856 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：4825 -
PC(聚碳酸酯)L-1250Y|嘉兴帝人|物性表参数嘉兴帝人Panlite PC L-1250Y 是一款熔融体积流量是8MVR，特性是 脱模性能良好, 中等粘性 ，通用级应用，在Japan实现工业化生产的聚碳酸酯树脂，长期以来，帝人一直致力于其性能的提高和
浏览量：4754 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：4707 -
PC(聚碳酸酯)PC-1100|乐天化学(LOTTE CHEMI···乐天化学的LOTTE Chemical HOPELEX PC PC-1100 是一种聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高强度、FDA/EU 食品容器认证，用于普通注塑产品。 以下是PC(聚碳酸酯)PC-1100/韩国乐天化学
浏览量：4578
推荐文章
-
FEP(聚全氟乙丙烯)100/科慕化学/物性表参数
科慕化学Teflon FEP 100是一种中等熔体流动速率的通用型聚全氟乙丙烯树脂，熔流率是7MFR（g/10 分钟）(测试条件ASTM D2116)，熔融温度260℃ (500°F)测试条件(ASTM，D4591/D3418)，应用于电线和电缆绝缘、小型管道、注塑成型部件。以下是FEP(聚全氟乙丙烯)100/科慕化学/物性表参数基本信息黄卡编号E54681-244676特性低摩擦系
-
PP(聚丙烯)HJ700|韩华道达尔(Hanwha)物性表参数
韩华道达尔(Hanwha)高抗冲PP HJ700是注塑用途的均聚PP，采用这一牌号生产的注塑部件具有高刚性和耐热性，以及优异的耐刮擦性能和表面光泽度,由于降低了挥发物含量，具有低气味特性，HJ700生产的产品可确保令人满意的服务品质.其特点是：高刚性、高耐热、优异的耐刮擦性能和表面光泽度、优异的感官性能和高洁净度(低VOC)。韩
-
PC(聚碳酸酯)LUX7430C/沙伯基础(SABIC)物性表参数
SABIC(沙伯基础创新塑料)LEXAN PC LUX7430C 是一种非填充，注塑成型等级,也是无氯化、无溴化阻燃剂PC,具有UL-94 V0等级为1.2 mm / 5VA等级为3.0mm，并具有UV稳定(F1等级)的额外抗老化能力,LEXAN LU
-
PC(聚碳酸酯)LGH2330M|三菱工程塑料|物性表参数
三菱工程塑料Iupilon PC LGH2330M是加15%弗素树脂和加30%玻纤复合强化,耐磨导电品级,体积熔融指数1.5厘米3/10分钟; 易脱模; 注塑成型,被广泛地用于各种工业生产，如运动器械、汽车部件、光学仪器、机械、办公自动化设备和电子设备，获得了客户的广泛信赖和支持。Iupilon PC LGH2330M物性表参数PDF文档下载以下是PC(聚
-
PC(聚碳酸酯)MN-4800Z|TEIJIN(帝人)物性表参数
TEIJIN(帝人)Panlite PC MN-4800Z 是一款熔融体积流量是6MVR cm/10min，特性是耐候性，脱模性能良好; 无溴; 阻燃性，应用于LEDs; 反射镜; 照明，Panlite在耐冲击性、耐热性、尺寸稳定性、电学特性、
-
PP(聚丙烯)HM3207|LUPOL(LG化学)物性表参数
LG化学的Lupol PP HM3207 是一款加20%矿物填料，耐气候级别的复合聚丙烯,熔融体积流量是10cm/10min,根据物理特性和加工方法其种类也多种多样,是具有代表性通用塑料中的一种，抗张强度
-
ARLEN(三井化学)C240N|PA6T(尼龙6T)物性表参数
三井化学ARLEN PA6T C240N是一种含有填充物为40%玻璃纤维增阻燃级尼龙6T材料,主要特性有:阻燃/额定火焰,是通过向其基本分子链中导入芳香环，在实现了320℃熔点的高耐热性的同时，也解决了以往聚酰胺树脂吸水性弱的问题,应用领域为:电气/电子应用。
-
PA66(尼龙66)FR370|Leona(尼胺龙)|旭化成|物性表参数
旭化成Leona(尼胺龙)PA66 FR370是一种阻燃等级UL94 V-0，不含卤素和磷的尼龙66材料，增强的抗焊接热性能，比重是1.16g/cm³，应用于接头，开关，其他电气和电子材料以下是PA66(尼龙66)FR370/Leona(尼胺龙)/旭化成/物性表参数物理性能干燥调节后的单位制测试方法比重1.16--
-
PP(聚丙烯)3210G4|惠州南亚塑胶|物性表参数
南亚塑胶工业（惠州）(Nan Ya Plastic)PP 3210G4是一种加入20%玻璃纤维增强PP(聚丙烯)树脂，比重轻，吸水性低，耐热性良好，产品用途：纱管，泵浦外壳，控制器外壳，家电产品等。以下是PP(聚丙烯)3210G4|惠州南亚塑胶|物性表参数基本性能额定值单位测试方法熔体流动速率4.0g/10minASTM D-1238物理性能额定值单位测试方法成型
-
ABS(丙烯腈丁二烯苯乙烯)FXS610SK|沙伯基础|物性表参数
SABIC(沙伯基础)CYCOLAC ABS FXS610SK是一种CYCOLAC FXS610SK是一种多用途ABS(丙烯腈丁二烯苯乙烯)注塑等级，提供了良好的工程性能平衡，CYCOLAC FXS610SK适用于需要闪光色彩效果的应用。CYCOLAC FXS610SK ABS物性表参数PDF文档下载以下是ABS(丙烯腈丁二烯苯乙烯)FXS610SK|沙伯基础|物性表参数物理性能额定值单位制测试方法