VALOX(沙伯基础)4012G/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX 4012G PBT是一种加10%玻璃纤维增强PBT注塑树脂，具有优异的机械性能,应用程序:连接器,该等级为4012，具有更好的循环时间和延展性。
 |
沙伯基础创新塑料的VALOX 4012G PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)4012G/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 80 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 80 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 4400 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3800 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 80 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 80 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 4500 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 125 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 120 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 5 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 3800 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 110 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 120 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 33 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 33 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 380 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 380 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 50 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 50 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 50 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 4 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 6 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 6 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 205 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 215 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 190 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 6.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 4.63E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 8.2E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 6.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 4.79E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 2.11E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 205 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 215 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 170 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 185 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.35 | - | ASTM D 792 | |
| Filler Content | 10 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.6-0.9 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.6-1.6 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.7-1 | % | SABIC method | |
| Melt Flow Rate, 250°C/1.2 kgf | 10 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 266°C/5.0 kgf | 90 | g/10 min | ASTM D 1238 | |
| Density | 1.35 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.2 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/1.2 kg | 9 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 50 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 80 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 110 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.4 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.015 | - | ASTM D 150 | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.4 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.015 | - | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 | |
| Comparative Tracking Index, M | 150 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Compliant, 94HB Flame Class Rating | 1.6 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 775 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 1.5 mm | 800 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 2.0 mm | 775 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 3.0 mm | 750 | °C | IEC 60695-2-13 | |
| Injection Molding | ||||
| Drying Temperature | 110-120 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250-270 | °C | ||
| Nozzle Temperature | 240-260 | °C | ||
| Front - Zone 3 Temperature | 245-265 | °C | ||
| Middle - Zone 2 Temperature | 240-255 | °C | ||
| Rear - Zone 1 Temperature | 230-245 | °C | ||
| Hopper Temperature | 40-60 | °C | ||
| Mold Temperature | 40-100 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：10052 -
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：9334 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：8614 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：7509 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：6930 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：6438 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：6096 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：5791 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：5750 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：5473 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：5337 -
COC(环烯烃共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一种烯烃聚合物(COP)具有优异的光学性能，可用于制造相机和激光打印机的光学部件，比重是1.01g/cm(ASTM D792)，熔流率（熔体流动速率）(280C/2.16 kg)是25g/10 min，ZEO
浏览量：5282 -
PA12(尼龙12)TR90|瑞士EMS化学|物性表参数科思德塑胶网站提供瑞士EMS化学PA12 TR90的物性表参数下载，并且有Grilamid PA12 TR90塑胶粒销售，为您提供详细的瑞士EMS化学PA12(尼龙12)TR90资料以及报价。
浏览量：5274 -
TRITAN(美国伊士曼)TX1501HF/PCTG(共聚聚酯···美国伊士曼TRITAN PCTG TX1501HF 是一种伊士曼TRITAN的高流动级材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相对于伊士曼TRITAN共聚酯TX1001，其他突出的特点包括良好的韧性，水解稳定性，耐热性
浏览量：5190 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：5173
推荐文章
-
SPS(间规聚苯乙烯)S131|出光兴产|物性表参数
出光兴产的XAREC SPS S131 是加30%玻璃纤维增强间规聚苯乙烯树脂，密度是1.25g/cm，拉伸模量是9700MPa，简支梁缺口冲击强度(23C)12kJ/m，UL阻燃等级 ( 0.800 mm) HB UL94，因分子规则排列，汽车,电子用
-
PA66(尼龙66)EPR27H/神马(Shenma)物性表参数
神马(Shenma)PA66EPR27H是一种中等粘度尼龙66，本品用于改善玻璃纤维的粘性，具有改善抗水不溶性的优点，可改善直接纺丝时的颜色粘性。以下是PA66(尼龙66)EPR27H/神马(Shenma)物性表参数产品特性中粘度技术参数物理性能值/单位测试标准测试条件粘度2.7 -Internalrelative visc温馨提示：本物性表参数提供者不承担任何
-
LEXAN(沙伯基础)4501/PC聚碳酸酯/物性表参数
SABIC的 LEXAN 4501 PC 是高耐热性的聚碳酸酯，在264 psi的情况下提供了290F的DTUL,对于一般的工程塑料来说虽然整体的强度比较好，但是化学性能和物理性能并不是特别的稳定，而且整体的使
-
PBT(聚对苯二甲酸丁二醇酯)S620F20|陶氏杜邦|物性表参数
陶氏杜邦Crastin S620F20 PBT 是根据良好的生产实践(GMP)原则生产的，并被广泛应用于食品接触领域在满足适用的使用条件时。杜邦 Crastin聚对苯二甲酸乙二醇酯 PBT 树脂具有高性价比
-
PC(聚碳酸酯)FR6009|科思创(Covestro)物性表参数
科思创(Covestro)的Makrolon PC FR6009是一种全球品级，中粘度的聚碳酸酯，体积熔融指数11.0厘米3/10分钟，高流动性能，带脱模剂，阻燃94-V0级别，抗UV聚碳酸酯，提高了耐化学性，应用于电子/电气;住宅部分。以下是PC(聚碳酸酯)FR6009|科思创(Covestro)物性表参数物理性能额定值单位制测试方法密度 (23°C)1.19g/cm³ISO 11
-
TPU(热塑性聚氨酯)2102/路博润(Lubrizol)物性表参数
路博润(Lubrizol)ESTANE TPU 2102是一种抗冲击改性热塑性聚氨酯，肖氏硬度有77A，84A,94A,58D,优势为耐化学性、水解稳定性和可混合性。以下是TPU(热塑性聚氨酯)2102/路博润(Lubrizol)物性表参数物理性能额定值 (公制)额定值 (英制)测试方法密度1.17 g/cc0.0423 lb/in³ASTM D792线性成型收缩率,Flow0.0040 - 0.0060 cm/cm0.
-
XYRON(采龙)L524V|旭化成|PPO(聚苯醚)物性表参数
旭化成XYRON PPO L524V 是一种加入40%填料阻燃级PPE/PS原料，特点: 良好的耐热性、尺寸稳定性和机械性能，应用领域: 汽车零件，电气和电子零件，工业零件，高性能等级实例: 具有很高
-
LEXAN(沙伯基础)HF1140/PC(聚碳酸酯)物性表参数
沙伯基础SABIC塑料 LEXAN HF1140 聚碳酸酯（PC） 是一种 良好的透明度，耐热性，保持性和尺寸稳定性， FDA食品接触有限颜色有限。 沙伯基础SABIC塑料LEXAN HF1140 PC物性表参数PDF文档下载 以下
-
PC(聚碳酸酯)ECF-9202/韩国乐天化学/物性表参数
韩国乐天化学的LOTTE Chemical HOPELEX PC ECF-9202 是一种聚碳酸脂塑料(Polycarbonate)，加碳素纤维 20%，特性是普通注塑成型材料。 以下是PC(聚碳酸酯)ECF-9202/韩国乐天化学/物性表参数 填料/增强材
-
ARLEN(三井化学)A335|PA6T(尼龙6T)物性表参数
三井化学ARLEN PA6T A335是一种含有填充物为35%玻璃纤维增尼龙6T材料,主要特性为:阻燃/额定火焰,是通过向其基本分子链中导入芳香环,在实现了320℃熔点的高耐热性的同时,也解决了以往聚酰胺树脂吸水性弱的问题。