PA6(尼龙6)BKV30H2.0/德国朗盛/物性表参数

日期：2020-04-14 09:49:52 编辑：科思德塑胶来源：科思德塑胶浏览：231

德国朗盛LANXESS Durethan PA6 BKV30H2.0是一种加入30%玻璃纤维，注塑，热老化稳定尼龙6树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
PA6 BKV30H2.0

以下是PA6(尼龙6)BKV30H2.0/德国朗盛/物性表参数

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	9600	5900
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	170	100
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.5	6.5
	Tensile creep modulus	1000 h	MPa	ISO 899-1		4100
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	80	95
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	70	70
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	15	20
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	10	10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	75	80
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	65	65
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	15	20
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	8500	5100
	Flexural strength	2 mm/min	MPa	ISO 178-A	280	170
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	4.0	6.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	265	140
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	~200
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	~215
	Temperature of deflection under load	8.00 MPa	°C	ISO 75-1,-2	~110
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	> 200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.2
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.8
	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
	Burning behavior UL 94	0.75 mm	Class	UL 94	HB
	Burning behavior US-FMVSS302	>=1.0 mm		ISO 3795	passed
	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	> 200
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	7.0
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	2.1
	Density		kg/m³	ISO 1183	1376
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	270-290
	Mold temperature		°C	-	80-120

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.

上一页：PA6(尼龙6)BKV30GW1/德国朗盛/物性表参数下一页：PA6(尼龙6)BKV30H2.0EF/德国朗盛/物性表参数

返回首页返回物性参数列表

PA6(尼龙6)BKV30H2.0/德国朗盛/物性表参数